PA6 GF33 Technical Specifications (Estimated)
| Eigendom | Waarde | Testnorm |
|---|---|---|
| Glasvezel inhoud | 33% (±2%) | ISO 1172 |
| Treksterkte | 135 – 185 MPa | ISO 527 |
| Flexural Modulus | 6,500 – 9,500 MPa | ISO 178 |
| Slagvastheid (ingekeepte Izod) | 11 – 15 kJ/m² | ISO 180 |
| Warmteafbuigingstemperatuur (HDT) | 180 – 200 °C @ 1.8 MPa | ISO 75 |
| Smeltpunt | 215 - 230 °C | ISO 3146 |
| Vochtabsorptie (evenwicht, 23°C/50% RH) | ~1.7% | ISO 62 |
PA6 Series Material Performance Comparison Table
| Eigendom | PA6 GF15 | PA6 GF30 | PA6 GF33 | PA6 GF40 | PA6 GF50 | PA6 GF60 |
|---|---|---|---|---|---|---|
| Glasvezel inhoud | 15% | 30% | 33% | 40% | 50% | 60% |
| Dichtheid (g/cm³) | 1.21 | 1.38 | ~1.42 | 1.46 | 1.56 | 1.67 |
| Treksterkte (MPa) | 118 | 165 | ~175 | 185 | 200 | 220 |
| Rek bij breuk (%) | 3.3 | 3.0 | ~2.9 | 2.8 | 2.0 | 2.0 |
| Ingeslagen schokweerstand (kJ/m²) | 10 | 12 | ~12.5 | 13 | 14 | 14 |
| Warmteafbuigingstemperatuur (℃, 1,8MPa) | 160 | 175 | ~195 | 215 | 216 | 220 |
Belangrijkste voordelen:.
Optimized Balance of Strength and Toughness
PA6 GF33 is engineered to offer a superior mechanical profile, delivering higher strength and rigidity than standard PA6 GF30, while maintaining better impact resistance and ductility compared to PA6 GF40. This makes it an ideal “upgraded” choice when GF30 is marginally insufficient.
Verbeterde mogelijkheden voor hoge temperaturen
With a Heat Deflection Temperature (HDT) typically elevated beyond that of GF30, PA6 GF33 provides improved performance and dimensional stability in demanding thermal environments, offering a safety margin for applications near the upper limit of GF30.
Superior Dimensional Stability and Precision
The increased fiber content further reduces moisture absorption and thermal expansion compared to GF30, resulting in enhanced dimensional stability for parts that require tight tolerances under varying environmental conditions.
Retained Processability
While requiring more robust processing parameters than GF30, PA6 GF33 generally maintains better melt flow and is less demanding on equipment than higher-load grades like GF40 or GF50, facilitating more reliable production.
Industriële toepassingen:
PA6GF33 is commonly used in automotive components, interior parts, and other applications that require a good surface finish and fundamental rigidity.
Aansturen van innovatie in verschillende sectoren
| Industrie | Belangrijkste toepassingen |
|---|---|
| Automotive | Motorkappen, inlaatspruitstukken, structurele steunen, sensorbehuizingen, connectoren. Ontdek Automobieltoepassingen → |
| Elektrisch & elektronica | Stroomonderbrekers, schakelaars, connectorbehuizingen, isolerende componenten. Ontdek E&E-oplossingen → |
| Industriële apparatuur | Tandwielen, lagers, machinebehuizingen, rollen, mechanische onderdelen. Zie Industrieel gebruik → |
Hoe kiezen?
Eenvoudig gezegd:
-
Voor goede taaiheid of kosteneffectiviteit, overweeg PA6 GF15.
-
Voor evenwichtige algemene prestaties, kiezen PA6 GF30.
-
Voor hogere stijfheid, sterkte en hittebestendigheid, en als de kosten minder gevoelig zijn, overweeg dan PA6 GF40/50/60. Over het algemeen verbetert een hoger glasvezelgehalte deze eigenschappen.
Waarom voor ons kiezen?
FAQ Sectie:
V: Kan ik een monster krijgen voordat ik een bestelling plaats?
A: Ja! We leveren gratis monsters voor gekwalificeerde projecten.
V: Wat is de productietijd?
A: Standaardkwaliteiten: 5-7 dagen; aangepaste formuleringen: 2-3 weken.
V: Leveren jullie materiaalcertificaten?
A: Ja, we leveren volledige materiaaldocumentatie en certificeringen.