PA6 GF33 Technical Specifications (Estimated)
| Propiedad | Valor | Norma de ensayo |
|---|---|---|
| Contenido en fibra de vidrio | 33% (±2%) | ISO 1172 |
| Resistencia a la tracción | 135 – 185 MPa | ISO 527 |
| Módulo de flexión | 6,500 – 9,500 MPa | ISO 178 |
| Resistencia al impacto (Notched Izod) | 11 – 15 kJ/m² | ISO 180 |
| Temperatura de deflexión térmica (HDT) | 180 – 200 °C @ 1.8 MPa | ISO 75 |
| Punto de fusión | 215 – 230 °C | ISO 3146 |
| Absorción de humedad (Equilibrio, 23°C/50% HR) | ~1.7% | ISO 62 |
PA6 Series Material Performance Comparison Table
| Propiedad | PA6 GF15 | PA6 GF30 | PA6 GF33 | PA6 GF40 | PA6 GF50 | PA6 GF60 |
|---|---|---|---|---|---|---|
| Contenido en fibra de vidrio | 15% | 30% | 33% | 40% | 50% | 60% |
| Densidad (g/cm³) | 1.21 | 1.38 | ~1.42 | 1.46 | 1.56 | 1.67 |
| Resistencia a la tracción (MPa) | 118 | 165 | ~175 | 185 | 200 | 220 |
| Elongation at Break (%) | 3.3 | 3.0 | ~2.9 | 2.8 | 2.0 | 2.0 |
| Notched Impact Strength (kJ/m²) | 10 | 12 | ~12.5 | 13 | 14 | 14 |
| Heat Deflection Temperature (℃, 1.8MPa) | 160 | 175 | ~195 | 215 | 216 | 220 |
Key Advantages：
Optimized Balance of Strength and Toughness
PA6 GF33 is engineered to offer a superior mechanical profile, delivering higher strength and rigidity than standard PA6 GF30, while maintaining better impact resistance and ductility compared to PA6 GF40. This makes it an ideal “upgraded” choice when GF30 is marginally insufficient.
Enhanced High-Temperature Capability
With a Heat Deflection Temperature (HDT) typically elevated beyond that of GF30, PA6 GF33 provides improved performance and dimensional stability in demanding thermal environments, offering a safety margin for applications near the upper limit of GF30.
Superior Dimensional Stability and Precision
The increased fiber content further reduces moisture absorption and thermal expansion compared to GF30, resulting in enhanced dimensional stability for parts that require tight tolerances under varying environmental conditions.
Retained Processability
While requiring more robust processing parameters than GF30, PA6 GF33 generally maintains better melt flow and is less demanding on equipment than higher-load grades like GF40 or GF50, facilitating more reliable production.
Aplicaciones industriales:
PA6GF33 is commonly used in automotive components, interior parts, and other applications that require a good surface finish and fundamental rigidity.
Impulsar la innovación en todos los sectores
| Industria | Aplicaciones clave |
|---|---|
| Automoción | Tapas de motor, colectores de admisión, soportes estructurales, carcasas de sensores, conectores. Explore las aplicaciones de automoción → |
| Electricidad y electrónica | Disyuntores, interruptores, carcasas de conectores, componentes aislantes. Descubra las soluciones E&E → |
| Equipamiento industrial | Engranajes, rodamientos, carcasas de máquinas, rodillos, componentes mecánicos. Véase Usos industriales → |
How to Choose?
En términos sencillos:
-
Para good toughness o cost-effectiveness, considera PA6 GF15.
-
Para balanced overall performance, elige PA6 GF30.
-
Para higher stiffness, strength, and heat resistance, and where cost is less sensitive, consider PA6 GF40/50/60. Generally, higher glass fiber content improves these properties.
¿Por qué elegirnos?
PREGUNTAS FRECUENTES Sección:
P: ¿Puedo obtener una muestra antes de hacer un pedido?
R: ¡Sí! Proporcionamos muestras gratuitas para proyectos cualificados.
P: ¿Cuál es el plazo de producción?
R: Grados estándar: 5-7 días; formulaciones personalizadas: 2-3 semanas.
P: ¿Proporcionan certificaciones de materiales?
R: Sí, proporcionamos documentación y certificaciones completas de los materiales.